Heat radiating plate and method for producing same

ABSTRACT

A heat radiating plate  10  of a metal material includes a flat plate portion  10   a , a large number of columnar protruding portions  10   b  which protrude from one major surface of the flat plate portion and which are integrated with the flat plate portion, and a reinforcing plate member  12  of a material, which has a higher melting point than that of the flat plate portion and columnar protruding portions and which is arranged in a region, which is arranged in the flat plate portion and which is close to one major surface of the flat plate portion, the reinforcing member passing through the flat plate portion to extend in directions substantially parallel to the one major surface of the flat plate portion and having end faces exposed to the outside, the whole surface of the reinforcing member except for the end faces being bonded directly to the flat plate portion.

CROSS-REFERENCE TO RELATED APPLICATION

This is a continuation application of U.S. patent application Ser. No. 14/036,551, filed Sep. 25, 2013, and entitled “HEAT RADIATING PLATE WITH SUPPORTING MEMBERS AND PROTRUSION MEMBERS”, the disclosure of which is incorporated by reference herein in its entirety as if set forth at length.

BACKGROUND OF THE INVENTION Field of the Invention

The present invention generally relates to a heat radiating plate and a method for producing the same. More specifically, the invention relates to a heat radiating plate integrated with radiating fins, and a method for producing the same.

Description of the Prior Art

In a conventional Metal/ceramic bonding substrate used as an insulating substrate for power modules, a metal circuit plate is bonded to one side of a ceramic substrate, and a metal base plate for heat radiation is bonded to the other side thereof, the metal circuit plate mounting thereon semiconductor chips and so forth.

In order to radiate heat from heating elements, such as semiconductor chips, to the outside, there is known a method for mounting radiating fins on the reverse of a metal base plate for heat radiation via radiating grease. There is also known a method for bonding radiating fins to a semiconductor device mounting substrate via a brazing filler metal (see, e.g., Japanese Patent Laid-Open No. 4-363052).

In order to further improve the cooling power of a metal/ceramic bonding substrate, there is proposed a heat radiator which has a member integrated with a large number of columnar (or pillar) protruding portions (as radiating fins), each of which has a shape of substantially circular truncated cone (see, e.g., Japanese Patent Laid-Open No. 2007-294891).

When a large number of columnar protruding portions having a shape of substantially circular truncated cone are formed as radiating fins like a heat radiator disclosed in Japanese Patent Laid-Open No. 2007-294891, if the protruding portions are formed by a method (so-called molten metal bonding method) for cooling and solidifying a molten metal (of aluminum, an aluminum alloy or the like) injected into a mold, a great thermal stress is produced during the cooling and solidifying of the molten metal by the great difference between the thermal expansion coefficient of the mold (of isotropic carbon or the like) and that of aluminum, the aluminum alloy or the like, so that it is very difficult to release the protruding portions from the mold if a large number of radiating fins having a small tapered angle (of not greater than 5°) are formed to increase the total surface area of the radiating fins. For that reason, there are problems in that it is not possible to obtain radiating fins having a desired shape due to the flaws and breaks thereof and/or that the mold is broken.

SUMMARY OF THE INVENTION

It is therefore an object of the present invention to eliminate the aforementioned problems and to provide a heat radiating plate, which can be easily released from a mold to form columnar (or pillar) protruding portions having a desired shape while preventing the break of the mold, even if the heat radiating plate produced by the mold has a flat plate portion integrated with a large number of protruding portions which protrude from one major surface of the flat plate portion, and a method for producing the same.

In order to accomplish the aforementioned and other objects, the inventors have diligently studied and found that it is possible to produce a heat radiating plate, which can be easily released from a mold to form columnar (or pillar) protruding portions having a desired shape while preventing the mold from being broken, even if the heat radiating plate produced by the mold has a flat plate portion integrated with a large number of protruding portions which protrude from one major surface of the flat plate portion, if a reinforcing member extending in directions substantially parallel to the one major surface of the flat plate portion is arranged in a region which is arranged in the flat plate portion and which is close to the one major surface of the flat plate portion, in the heat radiating plate which is made of a metal and which has the flat plate portion integrated with the large number of protruding portions which protrude from the one major surface of the flat plate portion. Thus, the inventors have made the present invention.

According to one aspect of the present invention, there is provided a heat radiating plate which is made of a metal material and which comprises: a flat plate portion; a large number of columnar protruding portions which protrude from one major surface of the flat plate portion and which are integrated with the flat plate portion; and a reinforcing member which extends in directions substantially parallel to one major surface of the flat plate portion, the reinforcing member being arranged in a region which is arranged in the flat plate portion and which is close to the one major surface of the flat plate portion.

In this heat radiating plate, the reinforcing member preferably passes through the flat plate portion to extend therein, and the whole surface of a portion of the reinforcing member passing through the flat plate portion to extend therein is preferably bonded directly to the flat plate portion. The reinforcing member preferably has end faces which are exposed to the outside, and the whole surface of the reinforcing member except for the end faces is preferably bonded directly to the flat plate portion. The reinforcing member is preferably a plate member, and may be a plurality of plate members which are spaced from each other to extend. The reinforcing member is made of a material which has a higher melting point than that of the metal material of the flat plate portion and the columnar protruding portions. The metal material of the flat plate portion and the columnar protruding portion is preferably aluminum or an aluminum alloy. In this case, the reinforcing member is preferably made of a metal which contains iron and at least one selected from the group consisting of nickel, cobalt, copper and manganese. Alternatively, the reinforcing member may be made of at least one ceramic selected from the group consisting of alumina, aluminum nitride, silicon nitride and silicon carbide. Each of the large number of columnar protruding portions preferably has a shape of substantially cylindrical or circular truncated cone, and may have a shape of substantially rectangular column or flat plate. The region close to the one major surface of the flat plate portion is preferably a region which is apart from the one major surface of the flat plate portion by 0.1 to 1.0 mm. One major surface of a ceramic substrate may be bonded directly to the other major surface of the flat plate portion, and a metal plate may be bonded directly to the other major surface of the ceramic substrate.

According to another aspect of the present invention, there is provided a method for producing a heat radiating plate which is made of a metal material and which has a flat plate portion and a large number of columnar protruding portions protruding from one major surface of the flat plate portion and being integrated with the flat plate portion, the method comprising the steps of: allowing end portions of a reinforcing member of a material, which has a higher melting point than that of the flat plate portion and the columnar protruding portions, to be supported on a mold; injecting a molten metal of a metal material into the mold so that the molten metal contacts the whole surface of the reinforcing member except for end portions thereof in the mold; and then, cooling and solidifying the molten metal for forming the flat plate portion and the large number of columnar protruding portions, which protrude from the one major surface of the flat plate portion and which are integrated with the flat plate portion, and for allowing the reinforcing member, which extends substantially parallel to the one major surface of the flat plate portion, to be arranged in a region, which is arranged in the flat plate portion and which is close to the one major surface of the flat plate portion, while allowing the reinforcing member to be bonded directly to the flat plate portion.

According to a further aspect of the present invention, there is provided a method for producing a heat radiating plate which is made of a metal material and which has a flat plate portion and a large number of columnar protruding portions protruding from one major surface of the flat plate portion and being integrated with the flat plate portion, the other major surface of the flat plate portion being bonded directly to one major surface of a ceramic substrate, the method comprising the steps of: allowing end portions of the ceramic substrate and end portions of a reinforcing member of a material, which has a higher melting point than that of the flat plate portion and the columnar protruding portions, to be supported on a mold so that the ceramic substrate is apart from the reinforcing member in the mold; injecting a molten metal of a metal material into the mold so that the molten metal contacts both major surfaces of the substrate and the whole surface of the reinforcing member except for end portions thereof in the mold; and then, cooling and solidifying the molten metal for forming a metal plate to allow the metal plate to be bonded directly to the other major surface of the ceramic substrate, and for forming the flat plate portion and the large number of columnar protruding portions, which protrude from the one major surface of the flat plate portion and which are integrated with the flat plate portion, and for allowing the reinforcing member, which extends substantially parallel to the one major surface of the flat plate portion, to be arranged in a region, which is arranged in the flat plate portion and which is close to the one major surface of the flat plate portion, while allowing the reinforcing member to be bonded directly to the flat plate portion.

In these methods for producing a heat radiating plate, the reinforcing member preferably passes through the flat plate portion to extend therein, and the whole surface of a portion of the reinforcing member passing through the flat plate portion to extend therein is preferably bonded directly to the flat plate portion. The end portions of the reinforcing member protruding from the flat plate portion are preferably removed. The mold preferably comprises an upper mold member and a lower mold member, and the end portions of the reinforcing member are preferably clamped between the upper mold member and the lower mold member to be supported on the mold. The reinforcing member is preferably a plate member, and may be a plurality of plate members which are spaced from each other to extend. The molten metal is a molten metal of aluminum or an aluminum alloy. In this case, the reinforcing member is preferably made of a metal which contains iron and at least one selected from the group consisting of nickel, cobalt, copper and manganese. Alternatively, the reinforcing member may be made of at least one ceramic selected from the group consisting of alumina, aluminum nitride, silicon nitride and silicon carbide. Each of the large number of columnar protruding portions preferably has a shape of substantially cylindrical or circular truncated cone, and may have a shape of substantially rectangular column or flat plate. The region close to the one major surface of the flat plate portion is preferably a region which is apart from the one major surface of the flat plate portion by 0.1 to 1.0 mm.

According to the present invention, it is possible a heat radiating plate, which can be easily released from a mold to form columnar (or pillar) protruding portions having a desired shape while preventing the break of the mold, even if the heat radiating plate produced by the mold has a flat plate portion integrated with a large number of protruding portions which protrude from one major surface of the flat plate portion.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be understood more fully from the detailed description given herebelow and from the accompanying drawings of the preferred embodiments of the invention.

However, the drawings are not intended to imply limitation of the invention to a specific embodiment, but are for explanation and understanding only.

In the drawings:

FIG. 1A is a perspective view of the first preferred embodiment of a heat radiating plate according to the present invention;

FIG. 1B is a plan view of the heat radiating plate of FIG. 1A;

FIG. 1C is a sectional view taken along line IC-IC of FIG. 1B;

FIG. 2A is a sectional view of a mold used for producing the heat radiating plate shown in FIGS. 1A through 1C;

FIG. 2B is a perspective view of a lower mold member of the mold of FIG. 2A;

FIG. 2C is a plan view of the lower mold member of the mold of FIG. 2A;

FIG. 2D is a bottom view of an upper mold member of the mold of FIG. 2A;

FIG. 3A is a sectional view of the second preferred embodiment of a heat radiating plate according to the present invention;

FIG. 3B is a plan view of the heat radiating plate of FIG. 3A (on the side of a metal/ceramic bonding substrate);

FIG. 4A is a sectional view of a mold used for producing the heat radiating plate shown in FIGS. 3A and 3B;

FIG. 4B is a perspective view of a lower mold member of the mold of FIG. 4A;

FIG. 4C is a plan view of the lower mold member of the mold of FIG. 4A;

FIG. 4D is a bottom view of an upper mold member of the mold of FIG. 4A;

FIG. 5A is a perspective view of the third preferred embodiment of a heat radiating plate according to the present invention;

FIG. 5B is a plan view of the heat radiating plate of FIG. 5A (on the side of columnar protruding portions);

FIG. 6 is a plan view of a first modified example of columnar protruding portions of a heat radiating plate in the first through third preferred embodiments; and

FIG. 7 is a plan view of a second modified example of columnar protruding portions of a heat radiating plate in the first through third preferred embodiments.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Referring now to the accompanying drawings, the preferred embodiments of a heat radiating plate and a method for producing the same according to the present invention will be described below in detail.

First Preferred Embodiment

FIGS. 1A through 1C show the first preferred embodiment of a heat radiating plate according to the present invention. FIG. 1A is a perspective view of a heat radiating plate in this preferred embodiment, FIG. 1B is a plan view of the heat radiating plate of FIG. 1A, and FIG. 1C is a sectional view taken along line IC-IC of FIG. 1B.

In this preferred embodiment, a heat radiating plate 10 is made of a metal material, such as aluminum or an aluminum alloy. As shown in FIGS. 1A through 1C, the heat radiating plate 10 comprises: a flat plate portion 10 a having a substantially rectangular planar shape; a large number of columnar (or pillar) protruding portions 10 b (serving as radiating fins) integrated with the flat plate portion 10 a so as to protrude from one major surface of the flat plate portion 10 a; and one or a plurality of reinforcing plate members (three elongated reinforcing plate members having rectangular planar and sectional shapes in this preferred embodiment) 12 of a metal or ceramic, which are arranged in the flat plate portion 10 a.

Each of the columnar protruding portions 10 b has a shape of substantially cylindrical or circular truncated cone (a shape obtained by cutting the upper end portion of a substantially circular cone in directions substantially parallel to the bottom face thereof). The protruding portions 10 b extend in directions substantially perpendicular to the major surface of the flat plate portion 10 a. The columnar protruding portions 10 b are arranged as a plurality of rows of columnar protruding portions 10 b. In each row, the columnar protruding portions 10 b are arranged at regular intervals. Each row of the columnar protruding portions 10 b linearly extends, and the rows of the columnar protruding portions 10 b are arranged in parallel to each other. Adjacent two rows of the columnar protruding portions 10 b are arranged so as to be shifted from each other by a half pitch (by half of a distance between the central lines (axes of the columnar protruding portions 10 b) of adjacent two rows of the columnar protruding portions 10 b). Thus, the larger number of columnar protruding portions 10 b are arranged so that the distance between the adjacent two of the columnar protruding portions 10 b is ensured. If the larger number of columnar protruding portions 10 b can be arranged so that the distance between the adjacent two of the columnar protruding portions 10 b is ensured, other arrangement may be adapted.

In this preferred embodiment, the flat plate portion 10 a has a thickness of about 3 to 10 mm. Each of the columnar protruding portions 10 b has, e.g., a root diameter (a diameter of the bottom face thereof) of 1 to 10 mm, preferably 1.5 to 8 mm, and a height of about 2 to 50 mm, preferably about 5 to 15 mm. The columnar protruding portions 10 b are arranged at intervals (or pitches) of about 2 to 10 mm, preferably about 3 to 7 mm (so as to be apart from each other by a distance about 2 to 10 mm, preferably about 3 to 7 mm, between the central lines of adjacent columnar protruding portions 10 b). Each of the columnar protruding portions 10 b has a tapered angle (an angle between the central line of each of the columnar protruding portions 10 b and the side face thereof) of 0.5 to 5°, preferably 1 to 3°. The number of the columnar protruding portions 19 b is, e.g., preferably about 20 to 1000, more preferably 50 to 1000.

The reinforcing members 12 pass through the interior of the flat plate portion 10 a from one of both end faces in width directions (lateral directions perpendicular to longitudinal directions and thickness directions) thereof to the other end face to extend in the width directions. The reinforcing members 12 are arranged in a region (a region close to a highest stress region between the heat radiating plate 10 and a mold 20 shown in FIGS. 2A through 2D), which is close to one major surface (a major surface on the side of the columnar protruding portions 10 b) of the flat plate portion 10 b of the heat radiating plate 10, so that the (apparent) thermal expansion coefficient of the one major surface (the major surface on the side of the columnar protruding portions 10 b) of the flat plate portion 10 a of the heat radiating plate approaches that of the mold 20. The reinforcing members 12 are preferably arranged in a region which is apart from the one major surface (the major surface on the side of the columnar protruding portions 10 b) of the flat plate portion 10 a by 20% or less of the thickness of the flat plate portion 10 a. In this preferred embodiment, the reinforcing members 12 are arranged in a region which is apart from the one major surface of the flat plate portion 10 b by a distance of preferably 0.1 to 1.0 mm, more preferably 0.15 to 0.8 mm, and most preferably 0.2 to 0.7 mm (since the distance is preferably 0.2 mm or more in order to allow the molten metal to be easily injected into the mold).

The both end faces of the reinforcing members 12 in longitudinal directions thereof (in width directions of the flat plate portion 10 a) are exposed to the outside. The whole surface of each of the reinforcing members 12 except for the both end faces thereof (the whole surface of a portion of each of the reinforcing members 12 passing through the flat plate portion 10 a to extend therein) is bonded directly to the flat plate portion 10 a. Thus, the reinforcing members 12 passing through the flat plate portion 10 a from one of both end faces in width directions thereof to the other end face to extend in the width directions are provided in the region close to the one major surface (the major surface on the side of the columnar protruding portions 10 b) of the flat plate portion 10 a, so that it is possible to easily release the heat radiating plate 10 from the mold 20 after the heat radiating plate 10 is produced by the mold 20.

Furthermore, the flat plate portion 10 a and the columnar protruding portions 10 b integrated therewith are preferably made of aluminum or an aluminum alloy from the standpoints of electric conductivity, thermal conductivity and reliability of bonding to a ceramic substrate (when the ceramic substrate is bonded to the other major surface of the flat plate portion 10 a of the heat radiating plate 10). The reinforcing members 12 are preferably made of a material which has a higher melting point than that of the flat plate portion 10 a and columnar protruding portions 10 b. If the reinforcing members 12 are made of a metal material, they are preferably made of a steel or iron containing metal, which is inexpensive and which has a high strength. The iron containing metal is preferably a metal which contains iron and at least one selected from the group consisting of nickel, cobalt, copper and manganese. If the reinforcing members 12 are made of a ceramic material, they are preferably made of at least one selected from the group consisting of alumina, aluminum nitride, silicon nitride and silicon carbide, and more preferably aluminum nitride in view of the heat radiating performance thereof.

The heat radiating plate 10 in the preferred embodiment shown in FIGS. 1A through 1C can be produced by a method comprising the steps of: allowing both end portions of each of the reinforcing members 12 in longitudinal directions thereof to be supported on the mold 20 so as to arrange the reinforcing members 12 in the mold 20 shown in FIGS. 2A through 2D; injecting a molten metal into the mold 20 so that the molten metal contacts the whole surface of each of the reinforcing members 12 except for both end portions in longitudinal directions thereof; and then, cooling the mold 20.

As shown in FIG. 2A, the mold 20 of carbon or the like comprises a lower mold member 22 and an upper mold member 24, each of which has a substantially rectangular planar shape.

As shown in FIGS. 2A through 2C, the top face of the lower mold member 22 has a recessed portion (a flat plate forming portion) 22 a for forming a portion of the flat plate portion 10 a on the side of the other major surface (the major surface on the opposite side to the columnar protruding portions 10 b) thereof. The upper portion of each of both side faces of the flat plate forming portion 22 a in width directions thereof has recessed portions (reinforcing member supporting portions) 22 b, each of which substantially has the same shape and size as those of a corresponding one of both end portions of a corresponding one of the reinforcing members 12 in longitudinal directions thereof and which are spaced from each other, for housing therein the both end portions thereof.

As shown in FIGS. 2A and 2D, the under surface (reverse face) of the upper mold member 24 has a recessed portion (a flat plate forming portion) 24 a for forming a portion of the flat plate portion 10 a on the side of the one major surface (the major surface on the side of the columnar protruding portions 10 b) thereof (a portion of the flat plate portion 10 a nearer to the columnar protruding portions 10 b than the reinforcing members 12). The bottom face of the recessed portion 24 a has a large number of recessed portions (columnar protrusion forming portions) 24 b for forming a large number of columnar protruding portions 10 b. The flat plate portion 10 a is designed to be formed in a space defined by the flat plate forming portion 24 a of the upper mold member 24 and the flat plate forming portion 22 a of the lower mold member 22. The reinforcing members 12 are designed to be clamped between the upper mold member 24 and the reinforcing member supporting portions 22 b of the lower mold member 22 when the lower mold member 22 is covered with the upper mold member 24 after the reinforcing members 12 are housed in the reinforcing member supporting portions 22 b of the lower mold member 22. When the reinforcing members 12 are thus clamped, it is possible to precisely fix the reinforcing members 12 at predetermined positions (at predetermined positions in directions along the major surface of the flat plate portion 10 a and in thickness directions thereof). The distance (the width of the flat plate portion 22 a) between the reinforcing member supporting portions 22 b for supporting both end portions of each of the reinforcing members 12 is preferably such a length that a corresponding one of the reinforcing members 12 is not deflected by the molten metal in the mold 20. For example, the distance is preferably 75 mm or less when the thickness of each of the reinforcing members 12 is 0.6 mm, and it may be longer when each of the reinforcing members 12 is thicker. Furthermore, the lower mold member 22 or the upper mold member 24 has an inlet (not shown) for injecting a molten metal into the flat plate forming portion 24 a from an injecting nozzle (not shown).

In order to use such a mold 20 for producing the preferred embodiment of a heat radiating plate shown in FIG. 1A through 1C, the reinforcing members 12 are put on the reinforcing member supporting portions 22 b of the lower mold member 22, and then, the lower mold member 22 is covered with the upper mold member 24. In this state, if a molten metal of aluminum, an aluminum alloy or the like is injected into the mold 20 and cooled, it is possible to produce the heat radiating plate wherein the reinforcing members 12 are arranged in the flat plate portion 10 a, wherein both end portions of the reinforcing members 12 in longitudinal directions thereof protrude from the side faces of the flat plate portion 10 a, and wherein the columnar protruding portions 10 b are integrated with one major surface of the flat plate portion 10 a. Thereafter, the both end portions of each of the reinforcing members 12 in the longitudinal directions thereof, the both end portions protruding from the flat plate portion 10 a, are cut by a well-known cutting method, so that it is possible to produce the heat radiating plate 10 in the preferred embodiment shown in FIGS. 1A through 1C. Furthermore, if dividing grooves (break lines) are previously and precisely formed at the cutting portions of the reinforcing members 12 by means of a laser, a scriber or the like, it is possible to easily divide and remove the both end portions of the reinforcing members 12 (by hand).

The molten metal is preferably injected into the mold 20 as follows. First, the mold 20 is moved into a furnace (not shown), and the interior of the furnace is caused to be in an atmosphere of nitrogen to decrease the oxygen concentration therein to 100 ppm or less, preferably 10 ppm or less. Then, the mold 20 is heated to a molten metal injecting temperature (e.g., 600 to 800° C. when a molten metal of aluminum or an aluminum alloy is injected) by the temperature control of a heater. Thereafter, while oxide films on the surface of a molten metal are removed, the molten metal, which is heated to the molten metal injecting temperature and which is previously measured, is pressurized at a predetermined pressure by nitrogen gas to be injected into the mold 20 from the inlet. After the molten metal is injected into the mold 20, nitrogen gas is preferably blown into the inlet from a nozzle (not shown) to cool and solidify the molten metal in the mold 20 while pressurizing the molten metal therein at a predetermined pressure. The predetermined pressure applied by nitrogen gas during the injection and cooling of the molten metal is preferably in the range of from 1 kPa to 100 kPa, more preferably in the range of from 3 kPa to 80 kPa, and most preferably in the range of from 5 kPa to 15 kPa. If the pressure is too low, it is difficult to allow the molten metal to be injected into the mold 20 (particularly into the columnar protrusion forming portions 24 b of the mold 20). If the pressure is too high, there is some possibility that the positions of the reinforcing members 12 may be shifted and/or the mold 20 may be broken. In particular, when a high pressure of not less than 1 MPa is applied if the mold 20 of carbon is used, there is some possibility that the mold 20 may be broken and/or the molten metal may leak from the mold 20 and/or the positions of the reinforcing members 12 may be shifted.

In this preferred embodiment, it is possible to radiate heat from heating elements if parts required to radiate heat from the heating elements, such as a metal/ceramic bonding substrate mounting thereon semiconductor chips and so forth, are mounted on the other major surface (the major surface on the opposite side to the columnar protruding portions 10 b) of the flat plate portion 10 a of the heat radiating plate 10.

Second Preferred Embodiment

FIGS. 3A and 3B show the second preferred embodiment of a heat radiating plate according to the present invention. FIG. 3A is a sectional view of the heat radiating plate in this preferred embodiment, and FIG. 3B is a plan view of the heat radiating plate of FIG. 3A (on the side of a metal/ceramic bonding substrate).

In this preferred embodiment, the same heat radiating plate as that in the first preferred embodiment is bonded to and integrated with parts required to radiate heat from the heating elements, such as a metal/ceramic bonding substrate mounting thereon semiconductor chips and so forth.

In this preferred embodiment, as shown in FIGS. 3A and 3B, a large number of columnar protruding portions 110 b are formed on one major surface of a flat plate portion 110 a of a heat radiating plate 110, and reinforcing members 112 are arranged in the flat plate portion 110 a thereof. One major surface of at least one (one in this preferred embodiment) ceramic substrate 114 is bonded to the other major surface (the major surface on the opposite side to the columnar protruding portions 110 b) of the flat plate portion 110 a of the heat radiating plate 110. The other major surface of the ceramic substrate 114 is bonded to a metal plate 116. Thus, the heat radiating plate 110 is integrated with and bonded to the metal/ceramic bonding substrate wherein the metal plate 116 is bonded to the ceramic substrate 114. When the metal/ceramic bonding substrate is integrated with and bonded to the heat radiating plate 110 as this preferred embodiment, the reinforcing members 112 are preferably arranged in a region which is apart from the one major surface (the major surface on the side of the columnar protruding portions 110 b) by a distance of 0.5 to 2.5 times as long as the thickness of the metal plate 116, and more preferably arranged in a region which is apart from the one major surface by a distance of 0.7 to 2 times as long as the thickness of the metal plate 116. Furthermore, in FIGS. 3A and 3B and in FIGS. 4A through 4D which will be described later, 100 is added to each of the reference numbers of portions having the same constructions as those of the heat radiating plate 10 in the above-described preferred embodiment.

The heat radiating plate 110 thus integrated with and bonded to the metal/ceramic bonding substrate can be produced by a method comprising the steps of: allowing the peripheral portion of the ceramic substrate 114 and both end portions of each of the reinforcing members 112 in longitudinal directions thereof to be supported on a mold 120 so as to arrange the ceramic substrate 114 and the reinforcing members 112 at a predetermined interval in the mold 120 shown in FIGS. 4A through 4D; injecting a molten metal into the mold 120 so that the molten metal contacts both sides of the ceramic substrate 114 and the whole surface of each of the reinforcing members 112 except for both end portions in longitudinal directions thereof; and then, cooling the mold 120.

As shown in FIG. 4A, the mold 120 of carbon or the like comprises a lower mold member 122 and an upper mold member 124, each of which has a substantially rectangular planar shape.

As shown in FIGS. 4A through 4C, the top face of the lower mold member 122 has a recessed portion (a flat plate forming portion) 122 a for forming a portion of the flat plate portion 110 a on the side of the other major surface (the major surface on the opposite side to the columnar protruding portions 110 b) thereof. The bottom face of the recessed portion 122 a has a recessed portion (a ceramic substrate housing portion) 122 c, which substantially has the same shape and size as those of the ceramic substrate 114, for housing therein the ceramic substrate 114. The bottom face of the recessed portion 122 c has a recessed portion (a metal plate forming portion) 122 d for forming a metal plate 116 for a circuit pattern. The upper portion of each of both side faces of the flat plate forming portion 122 a in width directions thereof has recessed portions (reinforcing member supporting portions) 122 b, each of which substantially has the same shape and size as those of a corresponding one of both end portions of a corresponding one of the reinforcing members 112 in longitudinal directions thereof and which are spaced from each other, for housing therein the both end portions thereof.

As shown in FIGS. 4A and 4D, the under surface (reverse face) of the upper mold member 124 has a recessed portion (a flat plate forming portion) 124 a for forming a portion of the flat plate portion 110 a on the side of the one major surface (the major surface on the side of the columnar protruding portions 110 b) thereof (a portion of the flat plate portion 110 a nearer to the columnar protruding portions 110 b than the reinforcing members 112). The bottom face of the recessed portion 124 a has a large number of recessed portions (columnar protrusion forming portions) 124 b for forming a large number of columnar protruding portions 110 b. The flat plate portion 110 a is designed to be formed in a space defined by the flat plate forming portion 124 a of the upper mold member 124 and the flat plate forming portion 122 a of the lower mold member 122. The reinforcing members 112 are designed to be clamped between the upper mold member 124 and the reinforcing member supporting portions 122 b of the lower mold member 122 when the lower mold member 122 is covered with the upper mold member 124 after the reinforcing members 112 are housed in the reinforcing member supporting portions 122 b of the lower mold member 122. When the reinforcing members 112 are thus clamped, it is possible to precisely fix the reinforcing members 112 at predetermined positions (at predetermined positions in directions along the major surface of the flat plate portion 110 a and in thickness directions thereof). The distance (the width of the flat plate portion 122 a) between the reinforcing member supporting portions 122 b for supporting both end portions of each of the reinforcing members 112 is preferably such a length that a corresponding one of the reinforcing members 112 is not deflected by the molten metal in the mold 120. For example, the distance is preferably 75 mm or less when the thickness of each of the reinforcing members 112 is 0.6 mm, and it may be longer when each of the reinforcing members 112 is thicker.

The upper mold member 124 has an inlet (not shown) for injecting a molten metal into the flat plate forming portion 129 a from an injecting nozzle (not shown). The lower mold member 122 has a molten metal passage (not shown) which extends between the flat plate forming portion 122 a and the metal plate forming portion 122 d for establishing a communication between the flat plate forming portion 122 a and the metal plate forming portion 122 d even if the ceramic substrate 114 is housed in the ceramic substrate housing portion 122 c.

In order to use such a mold 120 for producing a heat radiating plate 110, which is integrated with and bonded to a metal/ceramic bonding substrate, as shown in FIGS. 3A and 3B, after the ceramic substrate 114 is arranged in the ceramic substrate housing portion 122 c of the lower mold member 122, the reinforcing members 112 are put on the reinforcing member supporting portions 122 b of the lower mold member 122, and then, the lower mold member 122 is covered with the upper mold member 124. In this state, if a molten metal of aluminum, an aluminum alloy or the like is injected into the mold 120 and cooled, it is possible to produce the heat radiating plate 110 which is integrated with and bonded to the metal/ceramic bonding substrate, wherein both end portions of each of the reinforcing members 112 in longitudinal directions thereof, the reinforcing members 112 being arranged in the flat plate portion 110 a, protrude from the side faces of the flat plate portion 110 a and wherein the columnar protruding portions 110 b are integrated with one major surface of the flat plate portion 110 a, the other major surface thereof being bonded directly to one side of the ceramic substrate 114, the other side thereof being bonded directly to the metal plate 116 for a circuit pattern. Thereafter, the both end portions of each of the reinforcing members 112 in the longitudinal directions thereof, the both end portions protruding from the flat plate portion 110 a, are cut by a well-known cutting method, so that it is possible to produce the heat radiating plate 110 in the preferred embodiment shown in FIGS. 3A through 3C.

The molten metal is preferably injected into the mold 120 as follows. First, the mold 120 is moved into a furnace (not shown), and the interior of the furnace is caused to be in an atmosphere of nitrogen to decrease the oxygen concentration therein to 100 ppm or less, preferably 10 ppm or less. Then, the mold 120 is heated to a molten metal injecting temperature (e.g., 600 to 800 when a molten metal of aluminum or an aluminum alloy is injected) by the temperature control of a heater. Thereafter, the molten metal, which is heated to the molten metal injecting temperature and which is previously measured, is pressurized at a predetermined pressure by nitrogen gas to be injected into the mold 120 from the inlet. If the molten metal is thus injected, it is possible to prevent large bonding defects from being produced between the metal and the ceramic. After the molten metal is injected into the mold 120, nitrogen gas is preferably blown into the inlet from a nozzle (not shown) to cool and solidify the molten metal in the mold 120 while pressurizing the molten metal therein at a predetermined pressure. The predetermined pressure applied by nitrogen gas during the injection and cooling of the molten metal is preferably in the range of from 1 kPa to 100 kPa, more preferably in the range of from 3 kPa to 80 kPa, and most preferably in the range of from 5 kPa to 15 kPa. If the pressure is too low, it is difficult to allow the molten metal to be injected into the mold 120. If the pressure is too high, there is some possibility that the positions of the reinforcing members 12 may be shifted and/or the mold 120 may be broken. In particular, when a high pressure of not less than 1 MPa is applied if the mold 120 of carbon is used, there is some possibility that the mold 120 may be broken and/or the molten metal may leak from the mold 120 and/or the positions of the reinforcing members 112 and ceramic substrate 114 may be shifted.

In order to form a metal circuit plate from the metal plate 116 of the metal/ceramic bonding substrate thus integrated with and bonded to the heat radiating plate 110, the metal plate 116 may be etched to form a circuit pattern. In order to enable the circuit pattern to be soldered, the circuit pattern may be coated with Ni plating or Ni alloy plating.

Third Preferred Embodiment

FIGS. 5A and 5B show the third preferred embodiment of a heat radiating plate according to the present invention. FIG. 5A is a perspective view of the heat radiating plate in this preferred embodiment, and FIG. 5B is a plan view of the heat radiating plate of FIG. 5A (on the side of columnar protruding portions).

In this preferred embodiment, as shown in FIGS. 5A and 5B, columnar protruding portions 210 b may be formed on one major surface of a flat plate portion 210 a of a heat radiating plate 210 so as to correspond to regions (heating element mounting regions) 218 (on the other major surface of the flat plate portion 210 a) on which parts required to radiate heat from heating elements, such as a metal/ceramic bonding substrate mounting thereon semiconductor chips and so forth, are arranged. Furthermore, in FIGS. 5A and 5B, 200 is added to each of the reference numbers of portions having the same constructions as those of the heat radiating plate 10 in the above-described preferred embodiment.

While each of the columnar protruding portions 10 b, 110 b and 210 b has a shape of substantially cylindrical or circular truncated cone in the above-described first through third preferred embodiments, it may have a shape of substantially rectangular column as shown in FIG. 6, or it may have a shape of substantially flat plate as shown in FIG. 7. Furthermore, in FIGS. 6 and 7, 300 and 400 are added to each of the reference numbers of portions having the same constructions as those in the above-described preferred embodiment, respectively.

While each of the heat radiating plates uses an air-cooled radiating fins (columnar protruding portions 10 b, 110 b, 210 b) in the above-described first through third preferred embodiments, each of the columnar protruding portions 10 b, 110 b and 210 b may be covered with a casing (not shown) to forma water-cooled heat radiator, in which a cooling fluid flows, in order to enhance the cooling power thereof.

Examples of a heat radiating plate and a method for producing the same according to the present invention will be described below in detail.

Example 1

First, there was prepared a mold of carbon having a similar shape to that of the mold 120 shown in FIGS. 4A through 4D, except that the number of reinforcing member supporting portions 122 b was changed from three pairs to one pair. There were also prepared a ceramic substrate 114 of aluminum nitride having a size of 90 mm×40 mm×0.6 mm, and a reinforcing member 112 of aluminum nitride having a size of 90 mm×56 mm×0.6 mm. Then, the ceramic substrate 114 was arranged in the ceramic substrate housing portion 122 c of the lower mold member 122 of the mold 120, and both end portions (having a length of 3 mm) of the reinforcing member 112 were arranged in the reinforcing member supporting portions 122 b of the lower mold member 122, respectively. Thereafter, the lower mold member 122 was covered with the upper mold member 124 of the mold 120 to be put in a furnace, and the interior of the furnace was caused to be in an atmosphere of nitrogen to decrease the oxygen concentration therein to 4 ppm or less. In this state, the mold 120 was heated to 720° C. by the temperature control of a heater, and then, a molten metal of aluminum having a purity of 99.9%, which was heated to 720° C. and previously measured, was poured into the mold 120 from the injecting nozzle mounted on the inlet of the mold 120 while being pressurized at 10 kPa by nitrogen gas to remove oxide films on the surface of the molten metal. Thus, the molten metal was filled in a space having a size of 115 mm×50 mm×5 mm defined by the flat plate forming port ion 122 a and the flat plate forming portion 124 a (having a depth of 0.4 mm) in the mold 120, and in the metal plate forming portion 122 d having a size of 88 mm×38 mm×0.4 mm via the molten metal passage formed in the lower mold member 122. Thereafter, nitrogen gas was blown into the inlet from the injecting nozzle to cool and solidify the molten metal in the mold 120 while pressurizing the molten metal at 10 kPa. Thus, by a so-called molten metal bonding method, there was produced a heat radiating plate wherein the reinforcing member 112 passed through the flat plate, portion 110 a in a region, in which one major surface of the reinforcing member 112 (the major surface on the side of the columnar protruding portions 110 b) was spaced from one major surface of the flat plate portion 110 a (the major surface on the side of the columnar protruding portions 110 b) by 0.4 mm, the reinforcing member 112 being bonded directly to the flat plate portion 110 a, both end portions of the reinforcing member 112 protruding from the side faces of the flat plate portion 110 a, wherein 128 columnar protruding portions 110 b were arranged on one major surface of the flat plate portion 110 a at intervals (pitches) of 5 mm, each of the columnar protruding portions 110 b having a shape of substantially circular truncated cone which had a root diameter (a diameter of a bottom face) of 4 mm, a height of 8 mm and a tapered angle of 2° (the total surface area of the columnar protruding portions 110 b being 7628 mm²), and wherein one major surface of the ceramic substrate 114 was bonded directly to the other major surface of the flat plate portion 110 a, and the metal plate 116 was bonded directly to the other major surface of the ceramic substrate 114. After the heat radiating plate was ejected from the mold 120, the both end portions of the reinforcing members 112 in longitudinal directions thereof, the end portions protruding from the flat plate portion 110 a, were removed (by dividing the both end portions by hand along break lines previously formed by laser processing) to produce a heat radiating plate 110 having a similar shape to that shown in FIGS. 3A and 3B.

Furthermore, when the heat radiating plate was ejected from the mold 120, after the lower mold member 122 was detached, the upper mold member 124 was fixed to a mold releasing apparatus, and a steel plate was arranged on the upper mold member 124 so as to contact thereto. Then, the steel plate was knocked by a knocker (for quantitatively making shocks on the mold to release the heat radiating plate from the mold) to evaluate the releasability of the heat radiating plate from the mold by the number of shocks until release, and the surfaces of the heat radiating plate and the mold were observed. As a result, it was possible to release the heat radiating plate from the mold by two shocks. There was no problem in the shapes of the flat plate portion and column protruding portions of the heat radiating plate, and the mold was not damaged.

Examples 2-4

There was produced a heat radiating plate 110 by the same method as that in Example 1, except that the columnar protruding portions 110 b had a height of 5 mm, a tapered angle of 5° and a total surface area of 5018 mm² in Example 2, that the columnar protruding portions 110 b had a height of 5 mm, a tapered angle of 3° and a total surface area of 5235 mm² in Example 3, and that the columnar protruding portions 110 b had a height of 5 mm and a total surface area of 5364 mm² in Example 4. Then, by the same method as that in Example 1, the releasability of the heat radiating plate was evaluated, and the surfaces of the heat radiating plate and the mold were observed. Asa result, it was possible to release the heat radiating plate from the mold by no shock (Example 2), one shock (Example 3) and two shocks (Example 4), respectively. In Examples 2 through 4, there was no problem in the shapes of the flat plate portion and column protruding portions of the heat radiating plate, and the mold was not damaged.

Examples 5-8

There was produced a heat radiating plate 110 by the same method as that in Example 1, except that the columnar protruding portions 110 b had a root diameter of 2 mm and a height of 4 mm, and were arranged at intervals (pitches) of 3 mm, the number of the columnar protruding portions 110 b being 363 so that the columnar protruding portions 110 b had a total surface area of 5405 mm² in Example 5, that the columnar protruding portions 110 b had a tapered angle of 3° and a total surface area of 7447 mm² in Example 6, that the columnar protruding portions 110 b had a root diameter of 2 mm, a height of 4 mm and a tapered angle of 5°, and were arranged at intervals (pitches) of 3 mm, the number of the columnar protruding portions 110 b being 363 so that the columnar protruding portions 110 b had a total surface area of 5065 mm² in Example 7, that the columnar protruding portions 110 b had a root diameter of 2 mm, a height of 4 mm and a tapered angle of 3°, and were arranged at intervals (pitches) of 3 mm, the number of the columnar protruding portions 110 b being 363 so that the columnar protruding portions 110 b had a total surface area of 5285 mm² in Example 8. Then, by the same method as that in Example 1, the releasability of the heat radiating plate was evaluated, and the surfaces of the heat radiating plate and the mold were observed. As a result, it was possible to release the heat radiating plate from the mold by no shock (Example 5), one shock (Example 6), one shock (Example 7) and no shock (Example 8), respectively. In Examples 5 through 8, there was no problem in the shapes of the flat plate portion and column protruding portions of the heat radiating plate, and the mold was not damaged.

Example 9

In order to produce a heat radiating plate having a similar shape to that shown in FIGS. 5A and 5B, there was used a mold of carbon having a similar shape to that of the mold 120 shown in FIGS. 4A through 4D, except that three ceramic substrate housing portions 122 c were arranged at intervals of 1 mm and that the metal plate forming portion 122 d was formed in each of the ceramic substrate housing portions 122 c. There were also prepared three ceramic substrates 214 of aluminum nitride having a size of 65 mm×60 mm×0.6 mm, and three reinforcing members 212 of aluminum nitride having a size of 59 mm×110 mm×0.6 mm. Then, the ceramic substrates 214 were arranged in the ceramic substrate housing portions 122 c of the lower mold member 122 of the mold 120, and both end portions (having a length of 5 mm) of each of the reinforcing members 212 were arranged in the reinforcing member supporting portions 122 b of the lower mold member 122, respectively, so that the reinforcing members 212 are spaced at intervals of 7 mm to substantially face the central portion of each of the ceramic substrates 214, respectively. Thereafter, the lower mold member 122 was covered with the upper mold member 124 of the mold 120 to be put in a furnace, and the interior of the furnace was caused to be in an atmosphere of nitrogen to decrease the oxygen concentration therein to 4 ppm or less. In this state, the mold 120 was heated to 720° C. by the temperature control of a heater, and then, a molten metal of aluminum having a purity of 99.9%, which was heated to 720° C. and previously measured, was poured into the mold 120 from the injecting nozzle mounted on the inlet of the mold 120 while being pressurized at 10 kPa by nitrogen gas to remove oxide films on the surface of the molten metal. Thus, the molten metal was filled in a space having a size of 220 mm×100 mm×4 mm defined by the flat plate forming portion 122 a and the flat plate forming portion 124 a (having a depth of 0.7 mm) in the mold 120, and in the metal plate forming portions 122 d having a size of 62 mm×57 mm×0.4 mm via the molten metal passage formed in the lower mold member 122. Thereafter, nitrogen gas was blown into the inlet from the injecting nozzle to cool and solidify the molten metal in the mold 120 while pressurizing the molten metal at 10 kPa. Thus, by the so-called molten metal bonding method, there was produced a heat radiating plate wherein the reinforcing members 212 passed through the flat plate portion 210 a in a region, in which one major surface of each of the reinforcing members 212 (the major surface on the side of the columnar protruding portions 210 b) was spaced from one major surface of the flat plate portion 210 a (the major surface on the side of the columnar protruding portions 210 b) by 0.7 mm, the reinforcing members 212 being bonded directly to the flat plate portion 210 a, both end portions of each of the reinforcing members 212 protruding from the side faces of the flat plate portion 210 a, wherein 662 columnar protruding portions 210 b were arranged in each of regions facing the heating element mounting regions (the regions in which the ceramic substrates 214 were bonded to the flat plate portion 210 a) on one major surface of the flat plate portion 210 a at intervals of 6 mm, each of the columnar protruding portions 210 b having a shape of substantially circular truncated cone which had a root diameter (a diameter of a bottom face) of 2.5 mm, a height of 8 mm and a tapered angle of 2°, and wherein one major surface of each of the ceramic substrates 214 was bonded directly to the other major surface of the flat plate portion 210 a, and the metal plate 216 was bonded directly to the other major surface of each of the ceramic substrates 214. After the heat radiating plate was ejected from the mold 120, the both end portions of the reinforcing members 212 in longitudinal directions thereof, the end portions protruding from the flat plate portion 210 a, were removed (by dividing the both end portions by hand along break lines previously formed by laser processing) to produce a heat radiating plate 210 having a similar shape to that shown in FIGS. 5A and 5B.

Furthermore, when the heat radiating plate was ejected from the mold 120, after the lower mold member 122 was detached, the upper mold member 124 was fixed to a mold releasing apparatus, and a steel plate was arranged on the upper mold member 124 so as to contact thereto. Then, the steel plate was knocked by a knocker (for quantitatively making shocks on the mold to release the heat radiating plate from the mold) to evaluate the releasability of the heat radiating plate from the mold by the number of shocks until release, and the surfaces of the heat radiating plate and the mold were observed. As a result, it was possible to release the heat radiating plate from the mold by two shocks. There was no problem in the shapes of the flat plate portion and column protruding portions of the heat radiating plate, and the mold was not damaged.

Examples 10-11

There was produced a heat radiating plate 210 by the same method as that in Example 9, except that the columnar protruding portions 210 b had a root diameter of 4 mm and a tapered angle of 5°, and were arranged at intervals of 12.5 mm, the number of the columnar protruding portions 210 b being 252 in Example 10, that the columnar protruding portions 210 b had a root diameter of 3 mm and a tapered angle of 3.5°, and were arranged at intervals (pitches) of 9 mm, the number of the columnar protruding portions 210 b being 544 in Example 11. Then, by the same method as that in Example 9, the releasability of the heat radiating plate was evaluated, and the surfaces of the heat radiating plate and the mold were observed. As a result, it was possible to release the heat radiating plate from the mold by one shock in Examples 10 and 11. In Examples 10 and 11, there was no problem in the shapes of the flat plate portion and column protruding portions of the heat radiating plate, and the mold was not damaged.

Comparative Examples 1-2

There was produced a heat radiating plate 110 by the same method as that in Example 1, except that the distance between one major surface of the reinforcing member 112 (the major surface on the side of the columnar protruding portions 110 b) and one major surface of the flat plate portion 110 a (the major surface on the side of the columnar protruding portions 110 b) was 2.7 mm, the columnar protruding portions 110 b having a height of 5 mm, a tapered angle 5° and a total surface area of 5018 mm² in Comparative Example 1 and that the distance between one major surface of the reinforcing member 112 (the major surface on the side of the columnar protruding portions 110 b) and one major surface of the flat plate portion 110 a (the major surface on the side of the columnar protruding portions 110 b) was 1.2 mm, the columnar protruding portions 110 b having a height of 5 mm, a tapered angle 5° and a total surface area of 5018 mm² in Comparative Example 2. Then, by the same method as that in Example 1, the releasability of the heat radiating plate was evaluated, and the surfaces of the heat radiating plate and the mold were observed. As a result, it was not possible to release the heat radiating plate unless 15 shocks (Comparative Example 1) and 8 shocks (Comparative Example 2) were made. In Comparative Examples 1 and 2, flaws and deformations on the columnar protruding portions (radiating fins) of the heat radiating plate were observed. Furthermore, although the mold was not damaged, there is every possibility that the mold may be damaged since the releasability was bad.

Comparative Example 3

There was produced a heat radiating plate 110 by the same method as that in Example 1, except that the distance between one major surface of the reinforcing member 112 (the major surface on the side of the columnar protruding portions 110 b) and one major surface of the flat plate portion 110 a (the major surface on the side of the columnar protruding portions 110 b) was 1.3 mm. Then, by the same method as that in Example 1, it was attempted to evaluate the releasability of the heat radiating plate and to observe the surfaces of the heat radiating plate and the mold. However, since it was not possible to release the heat radiating plate from the mold after 30 shocks were made by the mold releasing apparatus, the heat radiating plate was released from the mold by hand. As a result, the upper mold member 124 was broken (it was not possible to release the heat radiating plate from the mold unless the upper mold member 124 was broken). In addition, flaws and deformations on the columnar protruding portions of the heat radiating plate were observed.

As described above, in Examples 1 through 11, the reinforcing member 112 passing through the flat plate portion 110 a of the heat radiating plate 110 from one end face of the flat plate portion 110 a in width directions (perpendicular to longitudinal directions) thereof to the other end face thereof to extend in the width directions was arranged in a region (a region close to a highest stress region between the heat radiating plate 110 and the mold 120) which was close to one major surface (a major surface on the side of columnar protruding portions 110 b) of the flat plate portion 110 a of the heat radiating plate 110 so that the thermal expansion coefficient of the one major surface (the major surface on the side of the columnar protruding portions 110 b) approaches that of the mold 120. Therefore, even if the tapered angle of the columnar protruding portions (radiating fins) 110 b was small (not greater than 5°), the releasability of the heat radiating plate 110 from the mold 120 was good, and it was possible to form good heat radiating fins having excellent dimensional accuracy while it was possible to prevent the mold 120 of carbon from being damaged.

While the present invention has been disclosed in terms of the preferred embodiment in order to facilitate better understanding thereof, it should be appreciated that the invention can be embodied in various ways without departing from the principle of the invention. Therefore, the invention should be understood to include all possible embodiments and modification to the shown embodiments which can be embodied without departing from the principle of the invention as set forth in the appended claims. 

What is claimed is:
 1. A method for producing a heat radiating plate which is made of a metal material and which has a flat plate portion and a plurality of columnar protruding portions protruding from one surface of the flat plate portion and being integrated with the flat plate portion, said method comprising the steps of: allowing end portions of a reinforcing plate member of a material, which has a higher melting point than that of said flat plate portion and said columnar protruding portions, to be supported on a mold; injecting a molten metal of a metal material into the mold so that the molten metal contacts the whole surface of the reinforcing plate member except for end portions thereof in the mold; and then, cooling and solidifying the molten metal for forming the flat plate portion and the plurality of columnar protruding portions, which protrude from the one surface of the flat plate portion and which are integrated with the flat plate portion, and for allowing the reinforcing plate member, which extends parallel to the one surface of the flat plate portion, to be arranged inside the flat plate portion between the one surface and an opposite surface of the flat portion and to be closer to the one surface of the flat plate portion than the opposite surface of the flat portion so as to be apart from the one surface of the flat plate portion by 20% or less of a thickness of the flat plate portion, while allowing the reinforcing plate member to be bonded directly to the flat plate portion.
 2. A method for producing a heat radiating plate which is made of a metal material and which has a flat plate portion and a plurality of columnar protruding portions protruding from one surface of the flat plate portion and being integrated with the flat plate portion, the other surface of the flat plate portion being bonded directly to one surface of a ceramic substrate, said method comprising the steps of: allowing end portions of the ceramic substrate and end portions of a reinforcing plate member of a material, which has a higher melting point than that of said flat plate portion and said columnar protruding portions, to be supported on a mold so that the ceramic substrate is apart from the reinforcing plate member in the mold; injecting a molten metal of a metal material into the mold so that the molten metal contacts both surface of the substrate and the whole surface of the reinforcing plate member except for end portions thereof in the mold; and then, cooling and solidifying the molten metal for forming a metal plate to allow the metal plate to be bonded directly to the other surface of the ceramic substrate, and for forming the flat plate portion and the plurality of columnar protruding portions, which protrude from the one surface of the flat plate portion and which are integrated with the flat plate portion, and for allowing the reinforcing plate member, which extends parallel to the one surface of the flat plate portion, to be arranged inside the flat plate portion between the one surface and an opposite surface of the flat portion and to be closer to the one surface of the flat plate portion than the opposite surface of the flat portion so as to be apart from the one surface of the flat plate portion by 20% or less of a thickness of the flat plate portion, while allowing the reinforcing plate member to be bonded directly to the flat plate portion.
 3. The method for producing a heat radiating plate as set forth in claim 1 or 2, wherein said end portions of said reinforcing plate member protruding from said flat plate portion are removed.
 4. The method for producing a heat radiating plate as set forth in claim 1, wherein said mold comprises an upper mold member and a lower mold member, and said end portions of said reinforcing plate member are clamped between the upper mold member and the lower mold member to be supported on said mold.
 5. The method for producing a heat radiating plate as set forth in claim 1, wherein said molten metal is a molten metal of aluminum or an aluminum alloy.
 6. The method for producing a heat radiating plate as set forth in claim 5, wherein said reinforcing plate member is made of a metal which contains iron and at least one selected from a group consisting of nickel, cobalt, copper and manganese.
 7. The method for producing a heat radiating plate as set forth in claim 5, wherein said reinforcing plate member is made of at least one ceramic selected from a group consisting of alumina, aluminum nitride, silicon nitride and silicon carbide.
 8. The method for producing a heat radiating plate as set forth in claim 1, wherein said reinforcing plate member is apart from said one surface of said flat plate portion by 0.1 to 1.0 mm.
 9. The method for producing a heat radiating plate as set forth in claim 1, wherein each of said columnar protruding portions has a shape of cylindrical or circular truncated cone.
 10. The method for producing a heat radiating plate as set forth in claim 1, wherein each of said columnar protruding portions extends in directions perpendicular to the one surface of said flat plate portion.
 11. The method for producing a heat radiating plate as set forth in claim 1, wherein each of said columnar protruding portions has a bottom face having a diameter of 1 to 10 mm and a height of about 2 to 50 mm and wherein a distance between the central lines of adjacent two of said columnar protruding portions is 2 to 10 mm, and an angle between the central line of each of said columnar protruding portions and the side face thereof is 0.5 to 5°, the number of said columnar protruding portions being 20 to
 1000. 